Silicon electrode plate for plasma etching with superior durability

ABSTRACT

This silicon electrode plate for plasma etching is a silicon electrode plate for plasma etching with superior durability including silicon single crystal which, in terms of atomic ratio, contains 3 to 11 ppba of boron, and further contains a total of 0.5 to 6 ppba of either or both of phosphorus and arsenic.

TECHNICAL FIELD

This invention relates to a silicon electrode plate for plasma etching with superior durability.

This application claims priority from Japanese Patent Application No. 2004-108731 filed on Apr. 1, 2004 and Japanese Patent Application No. 2004-234961 filed on Aug. 12, 2004, the contents of which are incorporated herein by reference.

BACKGROUND ART

Generally, when manufacturing semiconductor integrated circuits, it is necessary to conduct etching on an interlayer insulating film formed on a silicon wafer. A plasma etching device is used in order to conduct etching on this silicon wafer having the interlayer insulating film (hereinafter referred to as a wafer), and silicon is used as the electrode material inside this device. As shown in the schematic explanatory view of a partial cross-section in FIG. 1, the silicon electrode plate for plasma etching has a structure provided with etching gas ejecting through-holes 5 arranged in parallel in the thickness direction of the silicon single crystal plate. This silicon electrode plate for plasma etching 1 is fixed approximately at the center inside a vacuum container (not illustrated). A wafer 4 is placed on a stand 6, and high frequency voltage is impressed while etching gas 7 flows toward the wafer 4 through the etching gas ejecting through-holes 5. Thereby, plasma 2 is generated between the silicon electrode plate for plasma etching 1 and the wafer 4, and this plasma is made to act upon the wafer 4 to etch the surface of the wafer 4.

When plasma etching is conducted using a silicon electrode plate for plasma etching 1, electrical charge concentration areas (edge portion on which electrical charge is concentrated) are generated locally at the terminal openings of the etching gas ejecting through-holes 5 that contact the plasma 2, and these portions are more subject to wear. With respect to the etching gas ejecting through-holes 5 which are provided parallel to the thickness direction of the silicon electrode plate for plasma etching 1, as shown in FIG. 2, the opening of the etching gas ejecting through-holes 5 that contacts the plasma 2 becomes enlarged as it wears away so that it widens toward the bottom. Thereby, abrasion holes 3 are formed.

In the conventional silicon electrode plates for plasma etching 1 which are composed of silicon single crystal plates, the abrasion holes 3 are easy to be generated, and the length α in which the etching gas ejecting through-holes 5 has uniform diameter is reduced due to the formation of the abrasion holes 3 by plasma etching operations. Thereby, the wafer etching tends to become irregular.

In order to solve the above problem, a silicon electrode plate for plasma etching has been offered that is made of silicon containing 0.01 ppm to 5 mass % of a dopant of any one element selected from among P, As, Sb and B. This silicon electrode plate for plasma etching composed of the doped silicon single crystal plate has superior electrical conductivity; thereby, the formation of abrasion holes 3 due to generation of localized electrical charge concentration areas is suppressed. Accordingly, it is said that abrasion of the etching gas ejecting through-holes 5 is reduced, the flow of etching gas becomes uniform, and the lifetime is extended (see Patent Document 1 or 2).

However, it is impossible to avoid generation of the above-described abrasion holes 3 due to the plasma etching over a long period of time. Moreover, since in-plane irregularities occur with respect to the generated amount of the abrasion holes 3 formed in the silicon electrode plate for plasma etching 1, with the growing demands in recent years to keep the density of the plasma 2 uniform and maintain a more uniform etching of the wafer 4, the time of use of one silicon electrode plate for plasma etching 1 must be kept short, and early replacement must be conducted. The replaced silicon electrode plates for plasma etching 1 are then scrapped, resulting in a wasteful mode of use.

(Patent Document 1) Japanese Patent Application, First Publication No. H8-371 79

(Patent Document 2) Japanese Patent Application, First Publication No. H10-17393

DISCLOSURE OF THE INVENTION

Problems to be Solved by the Invention

The present invention has been made in light of the foregoing circumstances, and its object is to offer a silicon electrode plate for plasma etching which has more superior durability with little wear (i.e., generation of abrasion holes) of the etching gas ejecting through-holes and with a small in-plane distribution of abrasion holes, even when plasma etching is conducted over a long period of time.

Means for Solving the Problems

As a result of research from the pertinent standpoint aimed at obtaining a silicon electrode plate for plasma etching having a more excellent durability with a small in-plane distribution of abrasion holes, the present inventors and others obtained the following research results.

(A) Compared to a silicon single crystal plate solely containing boron or phosphorus, a silicon electrode plate for plasma etching including a silicon single crystal plate which contains, in coexistence with boron, either or both of phosphorus and arsenic further reduces abrasion of etching gas ejecting through-holes, and decreases in-plane abrasion irregularities.

(B) It is preferable that the content thereof in terms of atomic ratio be within the range of boron: 3 to 11 ppba (parts per billion atoms), and either or both of phosphorus and arsenic: 0.5 to 6 ppba.

The present invention was made based on the above research results.

The silicon electrode plate for plasma etching of the present invention has superior durability and includes silicon single crystal that contains, in terms of atomic ratio, 3 to 11 ppba of boron, and further contains a total of 0.5 to 6 ppba of either or both of phosphorus and arsenic.

In terms of atomic ratio, in the case in which boron is less than 3 ppba or the total of either or both of phosphorus and arsenic is less than 0.5 ppba, the desired effect relating to the amount of abrasion is not obtained; on the other hand, in the case in which boron content exceeds 11 ppba or where the total content of either or both of phosphorus and arsenic exceeds 6 ppba, the in-plane distribution of the etching plate becomes irregular, leading to undesirable results. Consequently, the boron content and the total content of either or both of phosphorus and arsenic in the silicon electrode plate for plasma etching have been set to 3 to 11 ppba of boron, and a total of 0.5 to 6 ppba of either or both of phosphorus and arsenic.

Effects of the Invention

When this silicon electrode plate for plasma etching is used, the amount of abrasion of the through-pore-holes becomes uniform, and it is possible to conduct uniform plasma etching over a longer period than that in the conventional case. Consequently, the frequency of replacement of the silicon electrode plates for plasma etching due to plasma etching can be greatly reduced, and a major contribution can be made to the development of the semiconductor device industry.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic explanatory view of partial cross-section that serves to explain the conditions of use of a silicon electrode plate for plasma etching.

FIG. 2 is a sectional explanatory view that serves to explain abrasion conditions in the etching gas ejecting through-holes of a silicon electrode plate for plasma etching.

BRIEF DESCRIPTION OF THE SYMBOLS

1 silicon electrode plate for plasma etching

2 plasma

3 abrasion hole

4 wafer

5 etching gas ejecting through-holes

6 stand

7 etching gas

BEST MODE FOR CARRYING OUT THE INVENTION

Preferred embodiments of the present invention are described below.

EMBODIMENT 1

Si raw material with a purity of 11 N was melted, and initially doped with B and P so as to prepare a Si melt containing 1 to 15 ppba of B and 1 to 10 ppba of P. Using this Si melt, a silicon single crystal having a diameter of 300 mm was prepared by the CZ method. After circular cutting and slicing this ingot at a thickness of 8 mm by a diamond band saw, a silicon single crystal electrode substrate with a diameter of 290 mm and a thickness of 6 mm was prepared by grinding.

Etching gas ejecting through-holes with a diameter of 0.3 mm were formed at 5 mm intervals in this silicon single crystal electrode substrate, and then this silicon single crystal electrode substrate was immersed in a liquid mixture of hydrofluoric acid, acetic acid and nitric acid for 5 minutes so as to remove the surface machining layer; whereby were prepared silicon electrode plates for plasma etching of the present invention (hereinafter, electrode plates of the present invention) 1 to 14 containing B and P in the contents shown in Table 1, comparative silicon electrode plates for plasma etching (hereinafter, comparative electrode plates) 1 and 2, and conventional silicon electrode plates for plasma etching (hereinafter, conventional electrode plates) 1 and 2.

The B and P contents of these electrode plates were measured by the photoluminescence method, that is, a method in which an Ar laser is irradiated to a cooled sample, and a diffraction grating spectrometer is used to detect the excited photoluminescence.

Furthermore, wafers with a SiO₂ layer formed in the surface were prepared in advance by the CVD method. TABLE 1 Number of wafers subjected to etching Dopant concentration until end of life of (ppba) the electrode Classification B P plate (wafers) Electrode plates 1 3.0 1.0 21110 of the present 2 3.7 0.8 21080 invention 3 3.7 5.2 20756 4 4.0 2.0 22153 5 4.6 1.0 22197 6 5.0 0.9 23412 7 5.0 2.0 23213 8 6.1 1.3 21157 9 6.0 2.0 21995 10 6.4 3.5 21033 11 7.0 3.0 20816 12 8.0 4.4 23702 13 8.7 3.9 22983 14 10.7 5.8 21033 Comparative 1 2 0.3 18820 electrode plates 2 12.0 6.5 17455 Conventional 1 5 — 19020 electrode plates 2 — 5 17211

These electrode plates of the present invention 1 to 14, comparative electrode plates 1 and 2, and conventional electrode plates 1 and 2 were respectively set in plasma etching devices, and wafers in which a SiO₂ layer was formed were also set in the plasma etching devices.

The SiO₂ layers in the wafer surface were subjected to plasma etching under the following conditions, and usage life was set at the point where the length of the etching gas ejecting through-holes (the length of the part shown by α in FIG. 2) provided in the electrode plates of the present invention 1 to 14, the comparative electrode plates 1 and 2, and the conventional electrode plates 1 and 2 became 1 mm, and the number of wafers which had been subjected to etching treatment until the end of usage life was obtained The obtained results are shown in Table 1.

Internal pressure of chamber: 10⁻¹ Torr

Etching gas composition: 90 sccm of CHF₃+4 sccm of O₂+150 sccm of He

High frequency power: 2 kW

Frequency: 20 kHz

From the results shown in Table 1, it is clear that the electrode plates of the present invention 1 to 14 containing both B and P have a longer usage life than the conventional electrode plates 1 and 2 containing only B or P. Since the comparative electrode plates 1 and 2 containing B and P in amounts deviating from the scope of this invention have a short usage life, they are undesirable.

EMBODIMENT 2

Si raw material with a purity of 11 N was melted, and initially doped with B and As so as to prepare a Si melt containing 1 to 15 ppba of B and 1 to 10 ppba of As. Using this Si melt, silicon single crystal silicon having a diameter of 300 mm was prepared by the CZ method. After circular cutting and slicing this ingot at a thickness of 8 mm by a diamond band saw, a silicon single crystal electrode substrates with a diameter of 290 mm and a thickness of 6 mm was prepared by grinding.

Etching gas ejecting through-holes with a diameter of 0.3 mm were formed at 5 mm intervals in this silicon single crystal electrode substrate, and then this silicon single crystal electrode substrate was immersed in a liquid mixture of hydrofluoric acid, acetic acid and nitric acid for 5 minutes so as to remove the surface machining layer; whereby 5 were prepared electrode plates of the present invention 15 to 28, comparative silicon electrode plates 3 and 4, and conventional electrode plate 3.

The B and As contents of these electrode plates were measured by the photoluminescence method.

Furthermore, wafers with a SiO₂ layer formed in the surface were prepared in advance by the CVD method.

These electrode plates of the present invention 15 to 28, comparative electrode plates 3 and 4, and conventional electrode plate 3 were respectively set in plasma etching devices, and wafers on which a SiO₂ layer was formed were also set in the plasma etching devices.

As in Embodiment 1, the SiO₂ layer in the wafer surface was subjected to plasma etching under the following conditions, and usage life was set at the point where the length of the etching gas ejecting through-holes (the length of the part shown by α in FIG. 2) provided in the electrode plates of the present invention 15 to 28, comparative electrode plates 3 and 4, and conventional electrode plate 3 became 1 mm, and the number of wafers which had been subjected to etching treatment until the end of usage life was obtained. The obtained results are shown in Table 2.

Internal pressure of chamber: 10⁻¹ Torr

Etching gas composition: 90 sccm of CHF₃+4 sccm of O₂+150 sccm of He

High frequency power: 2 kW

Frequency: 20 kHz TABLE 2 Number of wafers subjected to etching Dopant concentration until end of life of (ppba) the electrode Classification B As plate (wafers) Electrode plates 15 3.0 0.9 20055 of the present 16 3.6 0.8 20987 invention 17 3.7 5.1 20884 18 4.0 2.0 21435 19 4.5 1.0 21978 20 5.1 0.9 22859 21 5.0 1.9 23181 22 6.0 1.2 20897 23 6.1 2.1 21098 24 6.4 3.5 21298 25 7.0 3.1 20534 26 8.1 4.5 23475 27 8.7 4.0 22845 28 10.7 5.9 21857 Comparative 3 2 0.4 18155 electrode plates 4 11.7 6.3 17211 Conventional 3 — 5 17324 electrode plates

From the results shown in Table 2, it is clear that the electrode plates of the present invention 15 to 28 containing both B and As have a longer usage life than the conventional electrode plate 1 of Table 1 containing only B and the conventional electrode plate 3 of Table 2 containing only As. Since the comparative electrode plates 3 and 4 containing B and As in amounts deviating from the scope of this invention have a short usage life, they are undesirable.

EMBODIMENT 3

Si raw material with a purity of 11 N was melted, and initially doped with B, P and As so as to prepare a Si melt containing 1 to 15 ppba of B and 1 to 10 ppba of P+As. Using this Si melt, silicon single crystal having a diameter of 300 mm was prepared by the CZ method. After circular cutting and slicing this ingot at a thickness of 8 mm by a diamond band saw, a silicon single crystal electrode substrates with a diameter of 290 mm and a thickness of 6 mm was prepared by grinding.

Etching gas ejecting through-holes with a diameter of 0.3 mm were formed at 5 mm intervals in this silicon single crystal electrode substrate, and then this silicon single crystal electrode substrate was immersed in a liquid mixture of hydrofluoric acid, acetic acid and nitric acid for 5 minutes so as to remove the surface machining layer; whereby were prepared electrode plates of the present invention 29 to 33, and comparative silicon electrode plates 5 and 6.

The B, P and As contents of these electrode plates were measured by the photoluminescence method.

Furthermore, wafers with a SiO₂ layer formed in the surface were prepared in advance by the CVD method.

These electrode plates of the present invention 29 to 33 and comparative electrode plates 5 and 6 were respectively set in plasma etching devices, and wafers on which a SiO₂ layer was formed were also set in the plasma etching devices.

As in Embodiment 1, the SiO₂ layers in the wafer surface were subjected to plasma etching under the following conditions, and usage life was set at the point where the length of the etching gas ejecting through-holes (the length of the part shown by α in FIG. 2) provide in the electrode plates of the present invention 29 to 33 and comparative electrode plates 5 and 6 became 1 mm, and the number of wafers which had been subject to etching treatment until the end of usage life was obtained. The obtained results are shown in Table 3.

Internal pressure of chamber: 10⁻¹ Torr

Etching gas composition: 90 sccm of CHF₃+4 sccm of O₂+150 sccm of He

High power: 2 kW

Frequency: 20 Hz TABLE 3 Number of wafers subjected to etching Dopant concentration until end of life of (ppba) the electrode Classification B P As P + As plate (wafers) Electrode 29 4.0 1.7 0.3 2.0 20084 plates of the 30 4.6 0.9 0.1 1.0 22114 present 31 6.3 3.1 0.3 3.4 20987 invention 32 7.0 2.7 0.4 3.1 20012 33 8.0 3.9 0.6 4.5 22876 Comparative 5 2 0.2 0.1 0.3 17233 electrode plates 6 12.0 6.5 0.7 7.2 16211

From the results shown in Table 3, it is clear that the electrode plates of the present invention 29 to 33 containing all of B, P and As have a longer usage life than the conventional electrode plate 1 of Table 1 containing only B, the conventional electrode plate 2 of Table 1 containing only P, and the conventional electrode plate 3 of Table 2 containing only As. Since the comparative electrode plates 5 and 6 containing B in amounts and P and As in total amounts which deviate from the scope of this invention have a short usage life, they are undesirable.

INDUSTRIAL APPLICABILITY

The silicon electrode plate for plasma etching of the present invention enables plasma etching that is more uniform over a longer period of time than the prior arts. Consequently, it is possible to greatly reduce the frequency of replacement of the silicon electrode plates for plasma etching due to plasma etching, and to greatly contribute to the developments of semiconductor devices. 

1. A silicon electrode plate for plasma etching with superior durability, the silicon electrode plate comprising silicon single crystal which, in terms of atomic ratio, contains 3 to 11 ppba of boron, and further contains a total of 0.5 to 6 ppba of either or both of phosphorus and arsenic. 